Magnetic properties and magnetic entropy changes of La _{1- <i>x</i>} Pr _<i>x</i> Fe _11.5 Si _1.5 compounds with 0 ≤ <i>x</i> ≤ 0.5

Abstract

Magnetic properties and magnetic entropy changes in LaFe11.5Si1.5 have been investigated by partially substituting Pr by La. It is found that La1-xPrxFe11.5Si1.5 compounds remain cubic NaZn13-type structures even when the Pr content is increased to 0.5, i.e. x = 0.5. Substitution of Pr for La leads to a reduction in both the crystal constant and the Curie temperature. A stepwise magnetic behaviour in the isothermal magnetization curves is observed, indicating that the characteristic of the itinerant electron metamagnetic (IEM) transition above TC becomes more prominent with the Pr content increasing. As a result, the magnetic entropy change is remarkably enhanced from 23.0 to 29.4 J/kg·K as the field changes from 0 to 5 T, with the value of x increasing from 0 to 0.5. It is more attractive that the magnetic entropy changes for all samples are shaped into high plateaus in a wide range of temperature, which is highly favourable for Ericsson-type magnetic refrigeration.