Structural phase transition in the perovskite-type layer compound (C3H7NH3)2PbCl4

Abstract

(C3H7NH3)2PbCl4 is a new member of the family of perovskite-type layer compounds. Calorimetric, X-ray diffraction, and dieletric measurements show the occurrence of a structural phase transition at Tc ≈ 339 K, from an orthorhombic room temperature phase (ORT) with space group Pnma (Z = 4) to a monoclinic high temperature phase (MHT) with space group P21/c (Z = 2). This phase transition is analyzed according to group theoretical methods; in many respects the structural change of (C3H7NH3)2PbCl4 at 339 K is similar to that observed previously in (CH3NH3)2 · MCl4 compounds (M = Mn, Cd) at high pressure and low temperature. (C3H7NH3)2PbCl4 est un nouveau dérivé faisant partie de la série bien connue des composés de structure bidimensionnelle de type pérovskite. Une étude par calorimétrie, diffraction RX et par mesures diélectriques montre que ce dérivé présente une transition de phase structurale à Tc ≈ 339 K faisant passer d'une structure orthorhombique basse température Pnma (Z = 4) à une structure monoclinique haute température P21/c (Z = 2). La transition a pu ětre analysée en terme de théorie de groupes. Le comportement transitionnel de ce dérivé présente de nombreuses similitudes avec celui affectant les composés de la série homologue (CH3NH3)2MCl4 (M = Cd, Mn) sous haute pression et à basse température.