Extensive study of giant magnetoresistance properties in half-metallic Co2(Fe,Mn)Si-based devices

Abstract

Fully epitaxial Co2FexMn1−xSi(CFMS)/Ag/Co2FexMn1−xSi current-perpendicular-to-plane giant magnetoresistive devices with various Fe/Mn ratios x and top CFMS layer thicknesses tCFMS were prepared. The highest magnetoresistance (MR) ratios, 58% at room temperature and 184% at 30 K, were observed in the sample with x = 0.4 and tCFMS = 3 nm. Enhancement of interface spin-asymmetry was suggested for x = 0.4 compared with that at x = 0. A MR ratio of 58% was also observed even in a very thin trilayer structure, CFMS(4 nm)/Ag(3 nm)/CFMS(2 nm), which is promising for a next-generation magnetic read sensor for high-density hard disk drives.