Internal friction of vacuum-deposited silver films

Abstract

Internal friction of vacuum-deposited silver films 2–4 μm thick was measured using the vibrating-reed method below room temperature in the frequency range 100–400 Hz. Two distinct relaxation peaks were observed, one at around 50 K and the other at around 140 K. The former has been identified as the Bordoni peak, which was very stable against annealing at temperatures as high as 500 °C. The latter is considered as one of the Hasiguti peaks, which completely disappeared through annealing at 400 °C.