Miniature Long-Term Evolution (LTE) MIMO Ferrite Antenna

Abstract

A long-term evolution (LTE) MIMO ferrite antenna was fabricated on Ni <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.5</sub> Mn <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.2</sub> Co <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.07</sub> Fe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2.23</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sub> ferrite substrate (14 × 7 × 3 mm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sup> ) and characterized for antenna performance. Measured return loss and isolation were -26 and -16.4 dB at 720 MHz, respectively. Correlation coefficient calculated from experimental S-parameters (S <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">11</sub> , S <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">22</sub> , S <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">12</sub> , and S <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">21</sub> ) was less than 0.02 in the LTE band. Three-dimensional peak gain at 746 MHz was measured to be -8.83 dBi for antenna 1 and -8.32 dBi for antenna 2. These low antenna gains are attributed to high magnetic loss of ferrite substrate. Performance simulation suggests that antenna gain can be further improved up to -3.14 dBi with the use of low-loss ferrite.