Applied Physics Letters · 1988 · 140 citations · 12 references
Natural SciencesMaterials SciencePhysicsCondensed Matter PhysicsSolid State PhysicsThin FilmsChemical Vapor DepositionSuperconducting MaterialsSuperconducting Thin FilmsCritical Current DensityCuprate SuperconductorsCurrent DensityHigh-temperature Superconducting FilmsHigh-temperature SuperconductivityHigh-temperature SuperconductorsThin-film SuperconductorsYttrium Barium Copper Oxide Films
High Tc superconducting YBa2 Cu3 O7−x films were prepared by chemical vapor deposition using β-diketonates of Y, Ba, and Cu as source materials. The films were epitaxially grown on SrTiO3 (100) substrates. The c-axis orientation perpendicular to the plane of the substrates was observed. A sharp resistive superconducting transition with Tc (R=0) at 84 K was obtained. The maximum critical-current density at 77 K was 2×104 A/cm2 .
12
Structure of the single-phase high-temperature superconductor YBa2Cu3O7−δ
Mark A. Beno, L. Soderholm, D. W. Capone et al. · Applied Physics Letters · 1987 · 665 citations