Iodine Release and Recovery, Influence of Polyiodide Anions on Electrical Conductivity and Nonlinear Optical Activity in an Interdigitated and Interpenetrated Bipillared-Bilayer Metal–Organic Framework

Abstract

{[Cu6(pybz)8(OH)2]·I5(–)·I7(–)}n (1), obtained hydrothermally by using iodine molecules as a versatile precursor template, consists of a cationic framework with two types of zigzag channels, which segregate I5(–) and I7(–) anions. The framework exhibits the first observed bipillared-bilayer structure featuring both interdigitation and interpenetration. 1 displays high framework stability in both acidic (HCl) and alkaline (NaOH) solutions. 1 slowly releases iodine in dry methanol to give [Cu6(pybz)8(OH)2](I–)2·3.5CH3OH (1′) and partially recovers iodine from cyclohexane to form [Cu6(pybz)8(OH)2](I–)2·xI2 (1″). Differences of up to 100 times in electrical conductivity and of 4 times in nonlinear optical activity (NLO) have been measured between 1 and 1′. This compound is one of few displaying multifunctionality, electrical conductivity, NLO, and crystal–crystal stability upon release and recovery of iodine. It is also unique in the iodine release from polyiodide anions in a metal–organic framework.