Experimental investigations of shear and elongational flow properties of polystyrene melts reinforced with calcium carbonate, titanium dioxide, and carbon black

Abstract

Abstract Shear and elongational flow measurements on polystyrene melts reinforced with small particles were carried out. The influences of loading level, particle size and surface treatment on shear viscosity, principal normal stress difference, and elongational viscosity were discussed. These systems exhibited yield values for both shear and elongational flow. Experimental values for the ratio of the tensile to the shear yield stress give satisfactory agreement with the predictions of the von Mises yield criterion. The yield value appears to increase with decreasing particle size and may be varied with surface treatment. The principal normal stress difference at fixed shear stress decreases with volume loading of particulates. The results are interpreted in terms of a system forming a gel due to interparticle forces, which is disrupted by a critical distortional strain energy.