DC conductivity and dielectric behaviour of cobalt-zinc ferrites

Abstract

DC conductivity and dielectric studies of CoxZn1−xFe2O4 (x = 0.32, 0.49, 0.79), BaFe12O19, and Mg0.25Zn0.75Fe2O4 are reported as a function of temperature and frequency. The lattice constant and the existence of a single phase are established from X-ray studies. The dielectric behaviour is attributed to the Maxwell-Wagner polarisation. A dispersion region is observed in one of the cobalt-zinc ferrites and the barium ferrite. Activation energies are calculated for these two ferrites from dielectric measurements. The conductivity of these ferrites is explained by the hopping mechanism. Activation energies and the transition temperatures are presented. Ergebnisse von Gleichstromleitfähigkeits- und dielektrischen Untersuchungen an CoxZn1−xFe2O4 (x = 0,32; 0,49; 0,79) BaFe12O19 und Mg0,25Zn0,75Fe2O4 in Abhängigkeit von der Temperatur und Frequenz werden mitgeteilt. Die Gitterkonstante und die Existenz einer einzelnen Phase werden aus den Röntgenuntersuchungen festgestellt. Das dielektrische Verhalten wird der Maxwell-Wagner-Polarisation zugeschrieben. Ein Dispersionsbereich in einem der Kobalt-Zink-Ferrite und der Barium-Ferrite wird beobachtet. Für diese beiden Ferrite werden aus den dielektrischen Messungen Aktivierungsenergien berechnet. Die Leitfähigkeit dieser Ferrite wird durch einen Hopping-Mechanismus erklärt. Aktivierungsenergien und Übergangstemperatur werden angegeben.