Mechanical properties of polyurethane/montmorillonite nanocomposite prepared by melt mixing

Abstract

Abstract Nanocomposites from polyurethane (PU) and montmorillonite (MMT) were prepared under melt‐mixing condition, by a twin screw extruder along with a compatibilizer to enhance dispersion of MMT. MMT used in this study was Cloisite 25A (modified with dimethyl hydrogenated tallow 2‐ethylhexyl ammonium) or Cloisite 30B (modified with methyl tallow bis‐2‐hydroxyethyl ammonium). Maleic anhydride grafted polypropylene (MAPP) was used as the compatibilizer. XRD and TEM analysis demonstrated that melt mixing by a twin‐screw extruder was effective in dispersing MMT through the PU matrix. The PU/Cloisite 30B composite exhibited better interlayer separation than the PU/Cloiste 25A composite. Nanoparticle dispersion was the best at 1 wt % of MMT and improved with compatibilizer content for both composites. Properties of the composites such as complex viscosity and storage modulus were higher than that of a pure PU matrix and increased with the increase in MMT content, but decreased with the increase in compatibilizer content. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007