Microstructure effects on high temperature fatigue crack initiation and short crack growth in turbine disc nickel-base superalloy Udimet 720Li

Materials ScienceEngineeringSuperalloyMechanical EngineeringShort Crack GrowthMicrostructure-strength RelationshipMicrostructure EffectsCrack FormationDynamic Crack PropagationHigh TemperatureLow-cycle FatigueMechanics Of MaterialsMicrostructure