Erbium emission in MOS light emitting devices: from energy transfer to direct impact excitation

Abstract

The electroluminescence (EL) at 1.54 μm of metal–oxide–semiconductor (MOS) devices withEr3C ions embedded in the silicon-rich silicon oxide (SRSO) layer has been investigated under different polarization conditions and compared with that of erbium doped SiO2 layers. EL time-resolved measurements allowed us to distinguish between two different excitation mechanisms responsible for the Er3C emission under an alternate pulsed voltage signal (APV). Energy transfer from silicon nanoclusters (Si-ncs) to Er3C is clearly observed at low-field APV excitation. We demonstrate that sequential electron and hole injection at the edges of the pulses creates excited states in Si-ncs which upon recombination transfer their energy to Er3C ions. On the contrary, direct impact excitation of Er3C by hot injected carriers starts at the Fowler–Nordheim injection threshold (above 5 MV cm(-1)) and dominates for high-field APV excitation.