The effect of alkalization and fiber loading on the mechanical properties of bamboo fiber composites, Part 1: — Polyester resin matrix

Abstract

Abstract Bamboo strips [10 cm × 1.5 cm × (1−1.5) mm] were treated with caustic solutions for 1 h at different concentrations e.g., 0, 10, 15, 20, and 25%. Bamboo strips reinforced polyester resin composites were fabricated by hand‐lay‐up technique using both alkali‐treated and untreated bamboo strips, using a room temperature curing system for the polyester resin. This study aims at the evaluation of the influence of caustic concentration on the mechanical properties of bamboo strips reinforced polyester resin composites at a constant 50% loading of reinforcement. Maximum improvement in property was achieved possibly with 20% of caustic treated strip reinforcements. Beyond 20%, there was degradation in all the strength properties because of failure in mechanical properties of the reinforcements itself. The effect of fiber loading variation upon mechanical properties was also studied. It was observed that superior mechanical properties were obtained with 60% filler loading. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009