A giant electrocaloric effect of a Pb<sub>0.97</sub>La<sub>0.02</sub>(Zr<sub>0.75</sub>Sn<sub>0.18</sub>Ti<sub>0.07</sub>)O<sub>3</sub> antiferroelectric thick film at room temperature
124
Citations
26
References
2014
Year
Materials ScienceRoom TemperatureMaterial AnalysisEngineeringElectronic MaterialsPhysicsFerroelectric ApplicationApplied PhysicsQuantum MaterialsCondensed Matter PhysicsSuperconductivityGiant Electrocaloric EffectSemiconductor MaterialThin Film Process TechnologyThin FilmsElectrical PropertyThin Film ProcessingElectrochemistry
A maximum Δ<italic>T</italic> of 53.8 °C at 5 °C was achieved at 900 kV cm<sup>−1</sup> for a PLZST AFE thick film.