In‐situ photopolymerization of oriented liquid‐crystalline acrylates, 3. Oriented polymer networks from a mesogenic diacrylate

Abstract

Abstract Synthesis, mesomorphism, orientation and photo‐initiated chain crosslinking of the liquid‐crystalline diacrylate 1,4‐phenylene bis{4‐[6‐(acryloyloxy)hexyloxy]benzoate} ( 1 ) are studied. Monomer 1 exhibits a broad nematic phase between 108 and 155°C and a monotropic smectic phase below 88°C. The monomer is uniaxially oriented in its nematic phase at a substrate which has been coated with polyimide and unidirectionally rubbed with tissue. At the transition temperature to the smectic phase the order parameter is measured to be 0,7. During polymerization, the ordering of the mesogens is frozen‐in, yielding a uniaxially crosslinked network. The clear films of oriented poly( 1 ) exhibit a birefringence Δ n between 0,12 and 0,15, depending on the polymerization temperature. In the highest oriented state of 1 a small reduction of the degree of order is observed during the crosslinking reaction, whereas at higher temperatures and lower ordering of 1 , the uniaxially orientation increases upon reaction. A special feature of the oriented networks is that the ordering is maintained while heating at high temperatures. The polymerization of the acrylate groups in the mesomorphic phases proceeds fast and to high conversion. Below 90°C the polymerization behaviour is similar to that of conventional isotropic diacrylates. Above 90°C the polymerization reaction of the liquid‐crystalline diacrylate proceeds faster than that of an isotropic diacrylate.