Ultrasonic-assisted synthesis of Ce doped cubic–hexagonal ZnTiO3 with highly efficient sonocatalytic activity

Abstract

Ce doped ZnTiO3 as a novel catalyst with highly efficient and stable sonocatalytic activity was synthesized via an ultrasound-assisted sol-gel method using non-ionic surfactant Pluronic F127 as structure directing agent. Synthesized samples were characterized by using various techniques, such as XRD, TEM, SEM, EDX, ​XRF, BET, DRS, and PL, and their sonocatalytic activity studied toward degradation of p-Nitrophenol as a model organic compound. The synthesized mesoporous Ce/ZnTiO3 had mixed cubic-hexagonal phase with large surface area (118.2 m(2) g(-1)) and narrow pore size distribution (4.9 nm). The effects of cerium concentration, calcination temperature, and calcination time on the structure and the sonocatalytic activity of Ce/ZnTiO3 were studied in detail. XRD results were suggested that the relation between the phase structure and the catalytic activity is considerable. Significant decrease in band-gap and PL intensity was observed with increasing the cerium concentration in the ZnTiO3. It became clear that the Ce/ZnTiO3 (0.81 mol%) shows high sonocatalytic activity compared with pure ZnTiO3 and other Ce/ZnTiO3 samples as well as commercial TiO2-P25. The possible mechanism for the enhanced sonocatalytic activity of Ce/ZnTiO3 was discussed in details. The electrical energy consumption was also considered during sonocatalytic experiments.