${\rm MgB}_{2}$ for MRI Magnets: Test Coils and Superconducting Joints Results

Abstract

Among key design and operation issues for MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> relevant to MRI magnets are: uniformity of current-carrying capacity over long lengths (>;2 km) of wire; and reliability of a splicing technique. This paper presents experimental results of current-carrying capacities of a small test coil and joints, both made from MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> round wires, multifilament and monofilament (mono), manufactured by Hyper Tech Research, Inc. The test coils were wound with 95-m long unreacted, C (carbon)-doped MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> multifilament wire, sintered at 700°C for 90 min. The critical currents were measured in the 4.2 K-15 K and 0 T-5 T ranges. We have modified our original splicing technique, proven successful with unreacted, un-doped multifilament wire sintered at 570°, and applied it to splice both un-doped and C-doped mono wires sintered at 700°C. Most consistently good results were obtained using the un-doped mono wires. Also presented are results of a small joint-coil-PCS assembly of mono wire, operated in persistent mode at 50 A at >;10 K.