Co-doped anatase TiO2 nanofibers fabricated by electrospinning

Abstract

Co-doped TiO2 nanofibers with an average diameter of ∼70nm were fabricated with electrospinning method. X-ray diffraction measurements show that the nanofibers possess pure anatase structure. The obtained nanofibers exhibit evident room temperature ferromagnetism through magnetic measurement. The photoluminescence of the Co-doped TiO2 nanofibers is composed of two emission bands attributed to self-trapped excitons and oxygen vacancies, different from that of pure TiO2 nanofibers which only includes emission due to self-trapped excitons. Photoluminescence intensity due to oxygen vacancies vary with annealing atmosphere and Co concentration, and the ferromagnetic moment increases with the increment of oxygen vacancies.