Uniformity of Coronene-Added MgB <sub>2</sub> Superconducting Wires Fabricated Using an Internal Mg Diffusion Process

Abstract

We fabricated 100-m-long class-MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> superconducting wires using an internal Mg diffusion (IMD) process. Coronene was added as a carbon source to enhance the in-field critical current properties. We prepared a coil with a 4.8-cm diameter with 12 turns from a 2.6-m wire cut from the long wire. We obtained uniform critical currents (the critical current (I <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> ), the critical current density (J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> ), and engineering J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> (J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">e</sub> )) at different magnetic fields and temperatures, wire structures, compositions, and microstructures of the MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> layer in ten short wires cut from the middle ten turns of the coil. We also took seven pieces of a monofilament wire from the IMD long wire to fabricate a seven-filament IMD MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> wire, and we found no obvious decrease in J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> and J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">e</sub> when the diameter of the wires decreased from 1.06 to 0.88 mm. These results suggest that the IMD process could be used to fabricate MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> wires with a uniform structure. Coronene addition is useful for obtaining uniform composition and microstructure in the MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> layer because the B powder is uniformly coated with coronene for the whole wire during the annealing steps in the drawing process and the final heat treatment process. Therefore, the IMD process, together with coronene addition, is expected to fabricate MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> superconducting wires with uniform in-field critical current properties for practical large-scale applications.