Preparation of silicon carbide foams using polymeric precursor solutions

Abstract

A simple method was developed to produce silicon carbide foams using polysilane polymeric precursors. Polyurethane foams were immersed in polysilane precursor solutions to prepare pre-foams. Subsequently, these were heated in nitrogen at different temperatures in the range of 900°C to 1300°C. The silicon carbide foams produced in this manner showed well-defined open-cell structures and the struts in the foams were free of voids. The shrinkage which accompanies pyrolysis of the pre-foams was reduced with increasing the concentration of the polymeric precursor solutions.