Synthesis and Characterization of α‐NiMoO₄ Nanorods for Supercapacitor Application

Abstract

Abstract We report the synthesis of electrode materials based on one‐dimensional α‐NiMoO 4 nanorods for application as a supercapacitor. The structure and morphology of the electrodes were characterized by powder X‐ray diffraction, Raman analysis, X‐ray photoelectron spectroscopy, and scanning and transmission electron microscopy. The maximum specific capacitance obtained from electrochemical measurements on a standard three‐electrode system was 730 F g –1 at a scan rate of 5 mV s –1 . Furthermore, an asymmetric supercapacitor (ASC) was fabricated in which the NiMoO 4 nanorods were used as the positive electrode and reduced graphene oxide was used as the negative electrode. The maximum specific energy obtained from the ASC study was 12.31 Wh kg –1 at a specific current of 0.5 A g –1 in an aqueous KOH electrolyte. This ASC cell showed good stability with 85 % capacitance retention up to 2000 cycles. These results reveal that our ASC shows a high performance and specific energy as well as good cycling stability.