UV and visible light photocatalytic composite Pt and Au-TiO₂ coatings have been deposited on silicon and glass substrates at low temperature using a hybrid ECWR-PECVD/MS-PVD process. Methylene blue, stearic acid, and sulfamethoxazole were used as dye, organic, and antibiotic model pollutants, respectively, to demonstrate the efficiency of these nanocomposite coatings for water decontamination or self-cleaning surfaces applications. Raman investigations revealed the formation of anatase polymorph of TiO₂ in all synthesized coatings with a shifting of the main vibrational mode peak to higher wavenumber in the case of Au-TiO₂ coating, indicating an increase number of crystalline defects within this coating. Because of the difference of the chemical potentials of each of the investigated noble metals, the sputtered metal layers exhibit different morphology. Pt sputtered atoms, with high surface adhesion, promote formation of a smooth 2D layer. On the other hand, Au sputtered atoms with higher cohesive forces promote the formation of 5-10 nm nanoparticles. As a result, the surface plasmon resonance phenomenon was observed in the Au-TiO₂ coatings. UV photoactivity of the nanocomposite coatings was enhanced 1.5-3 times and 1.3 times for methylene blue and stearic acid, respectively, thanks to the enhancement of electron trapping in the noble metal layer. This electron trapping phenomenon is higher in the Pt-TiO₂ coating because of its larger work function. On the other hand, the enhancement of the visible photoactivity was more pronounced (3 and 7 times for methylene blue and stearic acid, respectively) in the case of Au-TiO₂ thanks to the surface plasmon resonance. Finally, these nanocomposite TiO₂ coatings exhibited also a good ability for the degradation of antibiotics usually found in wastewater such as sulfamethoxazole. However, a complementary test have showed an increase of the toxicity of the liquid medium after photocatalysis, which could be due the presence of sulfamethoxazole's transformation byproducts.

	Year	Citations

About